首頁

水性防銹膠玉磁漆

Water-Based Anti Rust Adhesive Jade Enamel

主要用于室內外、混凝土及墻璧紙裝修及保護。

關鍵字：

水性防銹膠玉磁漆

所屬分類 Category：

水性防腐鋼構漆系列

Waterborne anti-corrosion steel structure paint series

咨詢熱線 Tel：

13805008562

在線咨詢 Online consultation

產品詳情 Description

產品介紹

億翔水性防銹膠玉磁漆系列產品，由進口樹脂、優質顏填料、添加劑配制而成,以水為稀釋劑，無毒、無味、無污染，不燃不爆，配套體系完善,是傳統溶劑型鋼結構用漆的最佳換代產品。適用于輕型、高層、住宅、空間和橋梁鋼結構行業中冷彎成型、熱軋或焊接的結構部件(C型鋼、槽鋼、工字鋼、H型鋼等)的防護、防腐及裝飾。

施工方法:

刷涂、噴涂。
稀釋:

涂裝前應先將漆攪拌均勻若粘度偏高可加入適量清水，加水量不宜超過10%,應邊添加邊攪拌,保證漆液均勻。

基材處理:

涂裝前將工件表面得灰砂、焊渣、油污、浮銹及舊漆皮清除干凈。

施工環境：

施工時保持通風，不得在溫度低于5℃或濕度大于70%的狀況下施工。

建議涂裝遍數：

涂裝第二遍時，第一遍應干透，至少間隔24小時。

注意事歷：

漆膜可自干，也可低溫烘干，自干時溫度不低于5℃，濕度不大于70%，烘干時，流平時間不低于15分鐘。嚴禁與其他涂料及有機溶劑混合。

Product Introduction
The water-based anti rust adhesive jade enamel series products are formulated from imported resins, high-quality pigments and fillers, and additives. With water as the diluent, they are non-toxic, odorless, pollution-free, non flammable and non explosive, and have a complete supporting system. They are the best replacement products for traditional solvent based steel structure paints. Suitable for the protection, anti-corrosion, and decoration of structural components (C-shaped steel, channel steel, I-shaped steel, H-shaped steel, etc.) formed by cold bending, hot rolling, or welding in the light, high-rise, residential, spatial, and bridge steel structure industries.

Construction method:
Brushing and spraying.

Dilution:
Before painting, the paint should be stirred evenly. If the viscosity is too high, an appropriate amount of clean water can be added, and the amount of water should not exceed 10%. Mixing should be done while adding to ensure that the paint solution is even.

Substrate treatment:
Before painting, clean the surface of the workpiece of dust, welding slag, oil stains, floating rust, and old paint.

Construction environment:
Maintain ventilation during construction and do not operate at temperatures below 5 ℃ or humidity above 70%.

Recommended number of coats:
When applying the second coat, the first coat should be thoroughly dry, with a minimum interval of 24 hours.

Notes:
The paint film can be self dried or dried at low temperatures. When self drying, the temperature should not be lower than 5 ℃ and the humidity should not exceed 70%. When drying, the leveling time should not be less than 15 minutes. It is strictly prohibited to mix with other coatings and organic solvents.

生態環保水漆

水性鋼構漆